FP2500S halogen free flame retardant for PP PE TPE TPV

author:Novista  time:2023-8-23 16:42:22 visits:85 
FP2500S halogen free flame retardant for PP PE TPE TPV

PRODUCT DETAILS

ProFlame® PNPO-G3

 

 

PNPO-G3 is a halogen-free flame retardant , which develops its effectiveness through phosphorus /

nitrogen synergism. When incorporated into polymer, which can meet the requirement of UL94-V0(0.75-

1.6mm) and meet ROHS and REACH environmental regulations .

  

Benefits

Compared with bromine-antimony flame retardant, the product density is lower and the comprehensive cost of formula is lower

 With high thermal decomposition temperature , excellent heat aging resistance and excellent UV

stability, it can adapt to a wide range of processing technology and application

 Compared with traditional ammonimum polyphosphate flame retardant,it has excellent precipitation resistance and better hydrolysis resistance

 Low smoke density and low smoke gas corrosivity,good recyclability

 

Technical Data

Items                                                         Spec

Appearance                         White free-flowing powder

P content, %                                           18-22

1% TGA Temperature, °C                    260

D50 particle size, um                            10

Volatile,%                                                  1.0

Whiteness                                              90

 Bulk density,g/cm3                             0.40-0.60

 

 

 

Recommended dosage

 

Polymer

Recommended PNPO-G3 dosage

PP

UL94 V-0(1.5mm) - 20-26 wt% UL94 5VA(2.0mm) - 30-35 wt%

PP+30%GF

UL94 V-0(1.5mm) - 20-26 wt%

PE

UL94 V-0(1.5mm) - 28-32 wt%

TPE

UL94 V-0(1.5mm) - 32-35 wt%

TPV

UL94 V-0(1.5mm) - 37-39 wt%

Remark: For Non-glass-fiber system, it is recommended to add 0.2-0.4% anti-dripping agent

 

Processing instruction:

1.  The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components.

2.Both single- and twin-screw extruders are suitable for incorporating the product. The temperature of the polymer melt should not exceed 250°C.

3.Choosing proper filler and pigment .Calcium carbonate, carbon black, phthalocyanine green, zinc whitpowder will reduce Flame retardant efficiency               

 

Package & Storage:

Net weight 25KG Composite paper bag.

Minimum shelf life is 12 months stored in a dry and ventilated warehouse.