FR for PA nylon

OP1311 halogen free flame retardant HFFR for GF PA6

author:Novista  time:2023-8-23 11:06:33 visits:36 
OP1311 halogen free flame retardant HFFR for GF PA6

PRODUCT DETAILS

ProFlame® PN1131

ProFlame-PN1131 is formulated flame retardant based on organic phosphorus component. It is suited for both GF-reinforced and unreinforced PA6 /PA66 system. The polyamide compounds exhibit very good physical and electrical properties with PN1131.

 

Technical Data:
Items                                                                                       Spec

Appearance                                                              White free-flowing powde

Phosphorus content, %                                                            18-21

Decomposition Temperature, °C                                             350

Average particle size D50, um                                                 20-40

Moisture,%                                                                                    0.5

Whiteness                                                                                       95

 

 

Recommended dosage:

 

Polymer

PA6/PA66

UL-94

GWFI

Unreinforced

15-18

V0(0.75-1.6mm)

960°C

20-30%GF-Reinforced

15-20

V0(0.75-1.6mm)

960°C

 

Processing instruction:

1. Pre-drying the polyamide,the moisture content should be below 0.1 % (by wt.).

2.  The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components.

3.  The temperature of the polymer melt should not exceed 320 °C.

4.  It is most suitable for equipment with weak shear force.

5.  The processing temperature of Parallel twin-screw extruder should keep between 210 ~ 245  with

vacuum at the same time.The temperature is too high, the physical property loss of PA6 is large, and the yellowing is also large.

6. Do not use low-alkali or high-alkali fiberglass. High-quality non-alkali fiberglass is preferred.

 

 

Package & Storage:

Net weight 25KG Kraft bag with PE liner.

Minimum shelf life is 12 months stored in a dry and ventilated warehouse.