ProFlame® RTF-200
RTF-200 is a replacement of Sb2O3. It comply with ROHS & REACH environmental requirements. Especially recommended for styrene polymer(ABS,PS,AS,AEA,ASA), Epoxy resin polymer. In DBDPE/Sb2O3,FR245/ Sb2O3,Bromide epoxy/ Sb2O3, TBBA/ Sb2O3 Flame retardant System, It can completely replace antimony trioxide in the formula, maintain the same flame retardant grade and physical properties, and reduce the cost of the formula. It also can be used in PVC PP,PE and so on.
Physical and Chemical Index:
Product nam | RTF-200 |
Appearance | White powder |
Average Particle size,um | <20 |
Moisture,% | <0.1 |
As2O3,% | <0.04 |
PbO,% | <0.065 |
Fe2O3,% | <0.004 |
Se,% | <0.0015 |
CuO,% | <0.0035 |
►Flame retardant solution for ABS
Unit | Traditional Formula | 1# Formula | 2# Formula | 3# Formula | |
ABS Resin | % | 79 | 80 | 80 | 79 |
BN-9361 | % | 15 | 13 | 12.5 | 15 |
Sb2O3 | % | 5 | |||
RTF-200 | % | 6 | 6.5 | 5 | |
Anti-dripping KD-200 | % | 0.3 | 0.3 | 0.3 | 0.3 |
Other additives | % | 0.7 | 0.7 | 0.7 | 0.7 |
Function | Testing Standard | ||||
Tensile Strength(MPa) | ISO 527-1993 | 41 | 40.5 | 40.6 | 40.8 |
Elongation at break(%) | ISO 527-1993 | 6 | 8 | 7.9 | 7.2 |
Notch impact strength(kJ/m2) | ISO 180-2000 | 20 | 21 | 20 | 20 |
Flexural Strength(MPa) | ISO 178-2001 | 62 | 62 | 62 | 62 |
Flexural modulus(MPa) | ISO 178-2001 | 2200 | 2200 | 2200 | 2200 |
MFI (g/10min) | ISO 1133-2005 | 4 | 5 | 4.8 | 4.5 |
Density(g/cm3） | ISO 1183-2004 | 1.17 | 1.16 | 1.16 | 1.17 |
Flame Resistance(1.6mm) |
UL94 | V-0 | V-0 | V-0 | V-0 |
Flame Resistance(2.0mm) | V-0 | V-0 | V-0 | V-0 | |
Flame Resistance(3.2mm) | V-0 | V-0 | V-0 | V-0 |
►Flame retardant solution for HIPS
Units | Traditional Formula | 1# Formula | |
HIPS Resin | % | 83 | 83 |
B-044 | % | 12 | 10 |
Sb2O3 | % | 4 | |
RTF-200 | % | 6 | |
Anti-dripping KD-200 | % | 0.2 | 0.2 |
Other additives | % | 0.8 | 0.8 |
Testing Standard | |||
Tensile Strength(MPa) | ISO 527-1993 | 23 | 24 |
Elongation at break(%) | ISO 527-1993 | 30 | 30 |
Notch impact strength(kJ/m2) | ISO 180-2000 | 9.5 | 10 |
Flexural Strength(MPa) | ISO 178-2001 | 38 | 38 |
Flexural modulus(MPa) | ISO 178-2001 | 2500 | 2500 |
MFI (g/10min) | ISO 1133-2005 | 8 | 9 |
Density(g/cm3） | ISO 1183-2004 | 1.16 | 1.15 |
Flame Resistance(1.6mm) |
UL94-2006 | V-0 | V-0 |
Flame Resistance(2.0mm) | V-0 | V-0 | |
Flame Resistance(3.2mm) | V-0 | V-0 |
Package
25kg paper bag with PE liner bag.
Storage considerations:
The product can be stored under appropriate conditions for two years. But please keep products store in a dry ventilated environment (temperature should not exceed
30°C, in low humidity). Especially at high temperatures & high humidity, it is recommended not to stack more than 30 days long